聚十二烷二元酸酯及其共聚酯的合成

通过直接熔融缩聚法合成了一系列聚十二烷二元酸酯，用GPC、^1H—NMR、FTIR对产物进行了表征，并讨论了预聚酯合成时催化剂浓度和种类、预聚反应温度、预聚初始醇酸摩尔比对聚合反应的影响。结果表明，在所选的三个催化剂体系中，氮化亚锡二水合物与对甲苯磺酸复合催化剂的催化效果最好；最佳反应条件：n对甲苯横酯／n二元酸=0．0021～0．0032，反应温度为160～180℃，醇酸摩尔比范围为1．05—1.10。     

PET-HBT嵌段热致性液晶共聚酯的合成

液晶高分子材料具有相当高的强度和模量，被誉为当代超级工程塑料．以对羟基苯甲酸甲酯、1，4-丁二醇为主要原料，经熔融酯交换合成双-对羟基苯甲酸丁二醇酯(BBHB)；以四氯乙烷为溶剂，采用溶液缩聚法将过量的BBHB与对苯二甲酰氯(TPC)合成端基为BBHB的齐聚物(PHBT)；以对苯二甲酸二甲酯与乙二醇为原料，经熔融酯交换合成对苯二甲酸双β-羟乙酯(BHET)，然后采用溶液缩聚法将BHET与少量的TPC合成端基为TPC的齐聚物(PTET)；最后以PHBT与PTET为原料，以四氯乙烷为溶剂，采用溶液缩聚法合成目标共聚酯(PET-HBT)。研究了共聚酯的双折射现象及热行为；用偏光显微镜观察了试共聚酯的织态结构并用FTIR表征了共聚酯的微观结构．     

芳香族热致液晶聚（对羟基苯甲酸－对苯二甲酸双酚A酯）的流变性能

用Ｉｎｓｔｒｏｎ３２１１型毛细管流变仪研究了以对羟基苯甲酸（ＰＨＢ）、对苯二甲酸（ＴＰＡ）和双酚Ａ（ＢＰＡ）为单体合成的共聚芳酯液晶熔体的流变性能。结果表明，切变速率、熔体温度及ＰＨＢ链节含量对切粘度和结构粘度有很大的影响。切变速率在１０～１０３／Ｓ、温度２９５～３３０℃范围内，共聚酯粘流活化能△Ｅη为７４．５～２０５．１（ｋＪ／ｍｏｌ）。液晶熔体在剪切流中存在屈服应力τｏ，随温度升高τｏ值降低。在低温、低切变速率下，共聚酯熔体的弹性很小，甚至呈现挤出收缩现象。     

KINETICS OF NON-ISOTHERMAL CRYSTALLIZATION OF POLY (ETHYLENE TEREPHTHALATE) MODIFIED BY POLY (ETHYLENE GLYCOL)

The non-isothermal crystallization kinetics of poly(ethylene terephthalate) (PET) modified by poly (ethlene glycol) (PEG) were determined by DSC. The dual linear regression method was used to evaluate the relationship between the reciprocal of t 1/2 ( the half life of crystallization) and the appropriate temperature variable. The parameters such as the activation energy (Ed) for transport, the equilibrium melting temperature (T_m~0),the nucleation parameter (ψ),themaximum crystallization temperature (T_(e, max)), and the kinetic crystallizability (G) for the copolyesters were obtained. The influence of the PEG content in PET chains on the parameters characterizing crystallization kinetics and crystallization thermodynamics was discussed.     

有机磷化合物的质谱研究(Ⅶ)——二氮二磷杂环戊烷衍生物的化学电离质谱

本文报道了七种4.5-二氧代-2-硫代-1,3,2,4-二氮二磷杂环戊烷衍生物的化学电离质谱(CIMS,甲烷为反应气),结果表明:CIMS中准分子离子MH~+为基峰离子;MH~+离子易发生失去H_2S,CO,C_3H_6等小分子的裂解,(M+C_2H_5)~+离子存在再断裂。     

含柔性间隔基的热致液晶性共聚酯的结晶形态

采用偏光显微镜、扫描和透射电镜从不同层次的结构水平上研究了含柔性间隔基热致液晶性共聚酯的结晶形态。在偏光显微镜下观察到典型的负光性球晶形态,透射电镜揭示了球晶是由厚度为10nm并沿着径向生长的片晶结构所组成,分子链沿晶片厚度方向取向排列。并研究了分子链的刚性程度对热致聚芳酯结晶性质的影响。结果表明,分子链刚性越大其结晶性和球晶的完善性越高。     

Preparation and characterization of aliphatic/aromatic copolyesters based on 1,4-cyclohexanedicarboxylic acid

A series of biodegradable aliphatic/aromatic copolyesters, poly(butylene terephthalate)-co-poly(butylene cyclohexanedicarboxylate)-b-poly(ethylene glycol) (PTCG), were prepared by a two-step melt polycondensation method and characterized by means of GPC, FTIR, NMR, DSC, TGA, etc. The effects of aliphatic ester content on the physical, mechanical and thermal properties, as well as in vitro and in vivo degradation behaviors were investigated. The decrease in mechanical strength was observed with an increase in poly(butylene cyclohexanedicarboxylate) (PBC) molar fraction. DSC results showed one melting point and two glass transition temperatures in all samples, and the melting temperature was found to go down gradually as more cyclohexanedicarboxylic acid (CHDA) was added. During the in vitro and in vivo degradation processes, erosion of the surface was dominant as evidenced by scanning electron microscopic observations. The copolyesters containing many CHDA units were featured by the higher water uptake and faster degradation due to much richer amorphous phase within them.     

条带织构装饰技术观察含T─型液晶基元的热致性聚芳酯液晶态的向错

采用条带织构装饰新技术研究了含Ｔ─型液晶基元的热致性聚芳酯液晶态的向错形态．经过培养的液晶样品无需剪切，淬火后便可呈现出围绕向错点取向排列的条带织构，而条带织构长轴的垂直方向正代表了液晶基元的指向矢方向，这样，在普通偏光显微镜下就能直接观察到这些条带织构装饰的强度Ｓ＝±１／２和Ｓ＝±１的向错，并观察到Ｓ＝－３／２的高强度向错和闭环状的反转壁．     

Solubilities,thermostabilities and flame retardance behaviour of phosphorus-containing flame retardants and copolymers

Thirteen phosphorus-containing flame retardants were synthesized in this work. The solubilities of flame retardant [(6-oxide-6H-dibenz[c,e][1,2]oxaphosphorin-6-yl)-methyl]-butanedioic acid (DDP) in selected solvents are measured. TGA measurements of the 13 phosphorus-containing flame retardants were carried out and thermal stabilities of three flame-resistant PET (FRPET) resins were investigated. A FRPET incorporated by DDP with terephthalic acid and ethylene glycol reported in literature was also discussed and compared. The thermal stability of the FRPET is improved by the incorporation of phosphorus-containing flame retardants. The LOI values of all phosphorus-containing polyesters are higher than 27%. The improvement of the flame-resistant ability is due to the formation of the char that is not only caused by the existence of phosphorus elements in the resin but also by the relative large number of carbon atoms of the phenyl group in the flame retardants.